| Grade | Chemical Composition % | |||||||||
| Al≥ | impurities ≤ | |||||||||
| Si | Fe | Cu | Ga | Mg | Zn | Mn | others | Sum | ||
| Al99.9 | 99.90 | 0.50 | 0.07 | 0.005 | 0.02 | 0.01 | 0.025 | – | 0.010 | 0.10 |
| Al99.85 | 99.85 | 0.80 | 0.12 | 0.005 | 0.03 | 0.02 | 0.030 | – | 0.015 | 0.15 |
| Al99.7 | 99.70 | 0.10 | 0.20 | 0.010 | 0.03 | 0.02 | 0.030 | – | 0.030 | 0.30 |
| Al99.6 | 99.60 | 0.16 | 0.25 | 0.010 | 0.03 | 0.03 | 0.030 | – | 0.030 | 0.40 |
| Al99.5 | 99.50 | 0.22 | 0.30 | 0.020 | 0.03 | 0.05 | 0.050 | – | 0.030 | 0.50 |
| Al99.00 | 99.00 | 0.42 | 0.50 | 0.020 | 0.03 | 0.05 | 0.050 | – | 0.050 | 1.00 |
Aluminum
Aluminum Ingot
Aluminum Ingots
Aluminum Ingot 99.7%
Aluminum Ingot A7
Aluminum Alloy Ingot A356
Aluminum Alloy Ingot ADC12
Chemical Composition: Al
Weight: 20/25kg
Al (Min): 99%-99.9%
Place of Origin: China (Mainland)
Appearance: silvery white
Aluminum ingot for remelting is produced by molten salt electrolysis method using alumina and cryolite. Products meet the national standard GB/T1196-2002. The surface of ingot is clean and smooth.
Usage:
- mainly used for melting ingot
- discontinuous melting with scrap
- easy control and operation
- fast melting
- Used for industry such as automobile,pinning and weaving,electron broadly and so on
The main models are as follows: AL99.90, AL99.85, AL99.70A, AL99.70, AL99.60, AL99.50, AL99.00